TANKII A1 Similar Grade TKA-1 Fecral Alloys Wires Heating Resistance Alloy RESISTOHM 145 / ALLOY 875

Product Categories
Shanghai Tankii Alloy Material Co.,Ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Contact Now

TANKII A1 Similar Grade TKA-1 Fecral Alloys Wires Heating Resistance Alloy RESISTOHM 145 / ALLOY 875

Brand Name : TANKII

Model Number : TKA-1

Certification : ISO SGS

Place of Origin : Shanghai, China,

MOQ : Negotiable

Price : negotiable

Payment Terms : L/C, T/T, Western Union

Supply Ability : 200 Tons per Month

Delivery Time : 7-15 work days

Packaging Details : wooden case

Material : Alloy 875

Purity : 25%Cr, 6%Al

Surface : Bright / Polished / Oxidation / Golden

Density : 7.1g/cm3

Shape : Pipe/wire/rod/strip/plate/coil/foil

Contact Now

TANKII A1 Similar Grade TKA-1 Fecral Alloys Wires Heating Resistance Alloy RESISTOHM 145 / ALLOY 875​

TKA-1 large-sized cold-drawn wire products can be used for high-temperature resistance furnace. Practice has

proved that: the product process is stable, integrated performance is good. Has good high temperature oxidation

resistance and longer service life; excellent winding properties at room temperature processing, ease of

processing molding; little rebound resilience and so on. Processing performance is very good; operating

temperature can reach 1400 .

Conventional Product specifications: 0.5 ~ 10 mm

Properties Grade
 TKA-1
Cr Al Re Fe
25.0 6.0 Suitable Balance
Max Continuous ServiceTemperature(ºC) Diameter 1.0-3.0 Diameter large than 3.0,
1225-1350ºC 1400ºC
Resisivity 20ºC (Omm2/m) 1.45
Density(g/cm 3 ) 7.1
Approximate Melting Point( ºC) 1500
Elongation (%) 16-33
Repeatedly Bend Frequency(F/R)20ºC 7-12
Continuous Service Time under 1350ºC More than 60 hours
Micrographic Structure Ferrite

The relationship between the maximum operating temperature and the furnace atmosphere

Furnace atmosphere Dry Air Humid Air hydrogen-argon gas Argon Decomposition ammonia gas
Temp( ºC) 1400 1200 1400 950 1200

User Manual

  • Rated Voltage: 220V/380V
  • The installation process to avoid knocking, to avoid the damp, hand-held stove wire, they should wear gloves. Wire should be installed after the furnace has remained flat, and prevent surface scratches, dirt, corrosion, or improper installation, by affecting the life of
  • In the rated voltage to use. In strong reducing atmosphere, acid atmosphere, an atmosphere of high humidity will affect the use of life;
  • Temperature before use should be in dry non-corrosive atmosphere, about 1000 ℃ spend a few hours, so that furnace wire protective film formed on the surface after normal use, so that can guarantee the normal life of furnace wire;
  • Furnace installation should ensure that the insulated wire good power to avoid touching furnace after the wire, guard against electric shock or burns.

TANKII A1 Similar Grade TKA-1 Fecral Alloys Wires Heating Resistance Alloy RESISTOHM 145 / ALLOY 875


Product Tags:

high temperature metal alloys

      

high temperature wire

      
Quality TANKII A1 Similar Grade TKA-1 Fecral Alloys Wires Heating Resistance Alloy RESISTOHM 145 / ALLOY 875 for sale

TANKII A1 Similar Grade TKA-1 Fecral Alloys Wires Heating Resistance Alloy RESISTOHM 145 / ALLOY 875 Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Shanghai Tankii Alloy Material Co.,Ltd
*Subject:
*Message:
Characters Remaining: (0/3000)
 
You May Like